Comparison of the indentation strength and single-edge-v-notched beam methods for dental ceramic fracture toughness testing

Aim: To study influence of the cooling rate after sintering a veneering porcelain (Vita VM9) on fracture toughness by indentation strength (IS) and single-edge-v-notched beam (SEVNB) methods. Methods: Vita VM9 bars were sintered according to the manufacturer's recommendation and cooled under three conditions: Slow (inside the furnace from sintering temperature to room temperature); Normal (inside the furnace from sintering temperature to 500 ºC and outside the furnace from 500 ºC to room temperature); and Fast (outside the furnace from sintering temperature to room temperature). Fracture toughness was measured by IS (n=10) and SEVNB (n=10) methods. Data were analyzed by two-way ANOVA (α=0.05). Results: The fracture toughness obtained from SEVNB (slow - 1.02±0.10; normal - 1.09±0.13; and fast - 1,02±0.18 MPa.m1/2 cooling techniques) was significantly lower than IS (slow - 1.19±0.13; normal - 1.17±0.07; and fast - 1.16±0.06 MPa. m1/2 cooling techniques). There was no significant influence of the cooling technique (p=0.012). Conclusions: The measurement technique influenced the fracture toughness values . IS method overestimated the fracture toughness values. Irrespective of the measuring method, cooling rate did not influence the Vita VM9 veneering porcelain fracture toughness (Au)

Strength of 3Y-TZP and feldspathic porcelain subjected to different cooling methods

AIM: To investigate the effect of the cooling rate on flexural strength of monolayer and bilayer porcelain/zirconia (Y-TZP) bars. METHODS: Forty-five specimens were made for each design group: (PM) monolithic specimens of veneer porcelain Vita VM9 (Vita, Germany); (ZM) monolithic specimens of zirconia (ZiHP; ProtMat, Brazil); (PB) bilayer specimens zirconia/porcelain with porcelain on lower surface; and (ZB) bilayer specimens porcelain/zirconia with zirconia on lower surface. Each group was cooled by three different methods after porcelain sintering: slow specimens were cooled inside the turned-off furnace; normal specimens were removed from the furnace and cooled in air at room temperature; and fast specimens were removed from the furnace at 910°C and cooled by compressed air for 10 s. Specimens were polished and flexural strength was measured in water at 37 °C (n=15). Maximum load at fracture was recorded, and equations for simple (monolayer) and composite (bilayer) structures were used to calculate the flexural strength. RESULTS were analyzed using one-way ANOVA (p<0.05) and Tukey test separately for each design. RESULTS: The results of one-way ANOVA were statistically significant only for the PB group. The post-hoc Tukey test showed the highest flexural strength for fast cooling and the lowest for slow cooling; the normal cooling was statistically similar to both. CONCLUSIONS: Cooling methods affected only the flexural strength of bilayer specimens with porcelain on low surface (under tension) when the slow cooling method was used...

Effect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness.

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by two-way ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Effect of Carbamide Peroxide Bleaching Gel on Composite Resin Flexural Strength and Microhardness

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by two-way ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Este estudo investigou o efeito do peróxido de carbamida a 16% (Whiteness Perfect/FGM) na dureza Vickers e resistência à flexão dos compósitos restauradores Filtek Z100 (híbrida), Filtek Z350 (nanoparticulada), Brilliant (micro-híbrida) e Opallis (micro-híbrida). Espécimes em forma de disco (4x2 mm; n=5) e de barra (12x2x1 mm; n=10) de cada material restaurador foram distribuídos aleatoriamente em 2 grupos: (G1) 16 semanas em água destilada; (G2) armazenamento em água destilada durante 16 semanas, com aplicação do peróxido de carbamida a 16% por 6 h diárias nas últimas 4 semanas. As propriedades mecânicas foram avaliadas em microdurômetro Vickers e máquina de ensaios mecânicos. Os dados foram analisados por ANOVA a 2 critérios e teste de Tukey (α=0,05). Filtek Z100 apresentou o maior valor de dureza, seguido por Filtek Z350 e, finalmente, por Brilliant e Opallis (p=0,00). Filtek Z100 e Brilliant mostraram o maior valor de resistência à flexão, seguido por Filtek Z350 e Opallis (p=0,00). O clareamento diminuiu significantemente a dureza das resinas Brilliant e Opallis (p=0,00). A resistência à flexão dos materiais estudados não foi afetada pelo clareamento caseiro (p=0,28).

Resistência à flexão em porcelana feldspática: efeito da ciclagem mecânica e limite de fadiga pelo método escada / Flexural strength of feldspathic porcelain: effect of mechanical cycling and fatigue limit by the staircase method

Este estudo avaliou o limite de fadiga (LF), determinado pelo método escada, e o efeito da ciclagem mecânica sobre a resistência à flexão (RF) da porcelana feldspática Duceragold. Corpos de prova (25 x 5 x 2 mm) foram confeccionados de acordo com as instruções do fabricante e submetidos ao ensaio de RF (n = 10), em três pontos. Para determinação do LF (n = 30), foram utilizados carregamento inicial de 60% da RF, tensão incremental de 3% da RF, 10.000 ciclos e 2 Hz. Os dados foram submetidos à Anova e teste de Tukey (p < 0,05). Embora os ciclos propostos não tenham reduzido estatisticamente a RF, análises fractográficas evidenciaram estrias, sinais característicos de fadiga mecânica.

This study evaluated the fatigue limit (FL) by the staircase method and the effect of mechanical cycling on the flexural strength (FS) of Duceragold feldspathic porcelain. Specimens (25 x 5 x 2 mm) were made according to manufacturer’s directions and submitted to t hree-point fl exural s trength t est (n = 10). To d etermine FL (n = 30; 10,000 cycles; 2 Hz), an initial loading of 60% of the FS and an incremental loading (step) of 3% of the FS were used. Data were analyzed by Anova and Tukey´s test (p < 0.05). Although the proposed cycles have not reduced FS significantly, fractography analysis showed striation, characteristic signs of mechanical fatigue.

Efeito de diferentes taxas de resfriamento sobre a porcelana feldspática de cobertura para infraestruturas em zircônia / Effect of different cooling methods on a feldspathic porcelain veneer for zirconia core

A maior incidência de lascamentos na porcelana de cobertura é uma das principais desvantagens de restaurações com infraestrutura em zircônia se comparada com as metalocerâmicas. Essa maior ocorrência pode ser explicada por diferenças nas propriedades mecânicas das porcelanas indicadas para infraestrutura em zircônia ou por estresses residuais devido às propriedades térmicas dos materiais cerâmicos. Assim, este estudo apresentou os seguintes objetivos: 1. Comparar a resistência à flexão (MPa), confiabilidade pelo módulo de Weibull, dureza Vickers (VHN) e tenacidade à fratura (MPa/mm1/2) de duas porcelanas feldspáticas utilizadas sobre infraestrutura em zircônia (Vita VM9 e e.Max Ceram) e duas porcelanas feldspáticas utilizadas sobre infraestrutura metálica (Vita VMK95 e Duceragold); 2. Avaliar a resistência à fratura por flexão, confiabilidade, probabilidade de falha, dureza Vickers, tenacidade à fratura pelo método do entalhe em V e índice de cristalinidade por difratometria de raios-X de corpos-de-prova monocamada da porcelana Vita VM9 submetidos a três métodos de resfriamento; 3. Analisar a resistência à fratura por flexão, confiabilidade, resistência de cisalhamento da união e o modo de falha em corpos-de-prova bicamada de zircônia (ZrHP) e porcelana feldspática (Vita VM9) submetidos a diferentes taxas de resfriamento. No primeiro estudo, análises estatísticas de Kruskal Wallis e Dunn foram utilizadas(p<0,05). Não foi observada diferença estatística na resistência à flexão (p=0.31) entre as porcelanas. O módulo de Weibull apresentou maior confiabilidade para a porcelana VMK95 seguido por e.Max, Vita VM9 e Duceragold. No ensaio de dureza Vickers, as porcelanas e.Max, VM9 e VMK95 não apresentaram diferença estatística, enquanto a Duceragold apresentou o menor valor (p<0,001). O maior valor de tenacidade à fratura foi o da porcelana VMK95, enquanto a VM9 e a e.Max apresentaram valores mais baixos. Concluiu-se que, apesar da equivalência de resistência à flexão, confiabilidade e dureza, as porcelanas para infraestrutura em zircônia apresentaram menores valores de tenacidade a fratura, indicando uma possível explicação para a maior ocorrência de falhas. No segundo estudo, ao final do tempo de sinterização, os espécimes foram submetidos a três métodos de resfriamento: 1. Lento: deixados no interior do forno desligado por 8 horas; 2. Normal: retirados do forno e deixados resfriar à temperatura ambiente por 20 minutos; 3. Rápido: retirados imediatamente do forno e aplicado jato de ar comprimido por 10 segundos. Os dados foram analisados por análise de variância a um critério e teste de Tukey (p<0,05) e a análise de Weibull foi realizada a partir dos valores de resistência à flexão. Não houve diferença significativa para resistência à flexão (p=0,654) e tenacidade à fratura (p=0,734). No entanto, o resfriamento lento apresentou maior valor de dureza Vickers (p<0,001). O resfriamento normal apresentou maior módulo de Weibull, porém a resistência característica para o resfriamento rápido foi maior do que para normal e lento. A probabilidade de falha foi maior para as amostras do resfriamento normal e lento. O método de resfriamento rápido mostrou o menor índice de cristalinidade. No terceiro estudo, dados foram submetidos a ANOVA um fator, teste de Tukey(p<0,05) e análise de Weibull. A análise de variância para resistência à flexão para a configuração ZT não foi significativa (p=0,06), porém para configuração com a porcelana sob tração (PT) foi significativa, e o teste de Tukey revelou valores significativamente maiores para o resfriamento rápido(p<0,01). A análise de Weibull mostrou que o resfriamento normal apresentou confiabilidade ligeiramente maior. O resfriamento lento diminuiu a resistência de união (p<0,01) que mostrou padrão de fratura predominantemente coesiva e combinada, enquanto os demais métodos mostraram falha predominantemente adesiva. Esses estudos indicaram que as propriedades das porcelanas para zircônia podem diferir das indicadas para metalocerâmica e que o resfriamento da porcelana pode interferir em algumas propriedades de estruturas mono ou bicamada

The high incidence of chipping of the feldspathic porcelain veneer is one of the disadvantages of zirconia-based restorations in comparison to metal-based prosthesis. This highest occurrence may be explain by the difference in the mechanical proprieties of the porcelain to zirconia system or by the residual tensions due to thermal proprieties of ceramic materials. Then, the purpose of this study was: 1. To compare the three-point flexural strength (MPa), Weibull parameters, Vickers hardness (VHN) and Vickers indentation fracture toughness (MPa/mm1/2) of feldspathic porcelains for metal (Vita VMK95 and Duceragold) and for zirconia frameworks (Vita VM9 and e.Max Ceram); 2. To compare the flexural strength, reliability and probability of failure, measured by Weibull analysis, Vickers hardness, V-notch fracture toughness, and crystallinity index by Powder X-ray Diffractometry Technique of monolayer specimens of a dental feldspathic veneer porcelain for zirconia (VITA VM9) subjected to three different cooling conditions; 3. To investigate the effect of three cooling methods on the flexural strength, reliability, shear bond strength and failure mode of bilayer specimens of veneer porcelain (VITA VM9) and zirconia (ZrHP). In the first study, Kruskal-Wallis and Dun test were used for statistical analysis (p<0.05). There was no significant difference (p=0.31) among the porcelains in the flexural. Weibull calculation presented highest reliability for VMK95 followed by e.Max, VM9 and Duceragold. Vickers hardness test showed that e.Max, VM9 and VMK95 had no difference and Duceragold had the lowest value (p<.001). The highest fracture toughness was to VMK95, while VM9 and e.Max had the lowest values (p<.001). It was concluded that, despite of the suitable flexural strength, reliability and high hardness, the porcelains used to zirconia-based fixed dental prostheses showed lower fracture toughness values, indicating a possible explanation for the higher incidence of failures. In the second study, bar-shaped specimens made with Vita VM9 porcelain were sintered and cooled under three conditions: 1. Slow: left inside the switched-off furnace by 8 hours; 2. Normal: removed from the furnace and left cooling at room temperature by 20 minutes; and 3. Fast: removed immediately from the furnace and applied compressed air by 10 seconds. The data were analyzed by one-way ANOVA and Tukey's post hoc test (p<0.05). Weibull analysis was performed from flexural strength values. There were no significant differences in flexural strength values (p=0.654) or fracture toughness values (p=0.734). Nevertheless, one-way ANOVA was significant for Vickers hardness (p<0.001), and the Tukey's test showed that slow cooling had the highest mean value. Normal cooling showed highest Weibull modulus, however, the characteristic strength for fast cooling was higher than those for normal and slow cooling. The probability of failure was higher for the normal and slow cooling samples. Fast cooling method showed the lowest crystallinity index. In the third study, data were submitted to one-way ANOVA, Tukey's post hoc tests (p<0.05) and Weibull analysis. One-way ANOVA for the ZT configuration was not significant (p=0.06). However, ANOVA for the PT configuration, in which, the porcelain was under tension, was significant, and Tukey's test revealed that fast cooling leads to significantly higher values (p<0.01) than the other cooling methods. Weibull analysis showed that normal cooling had slightly higher reliability. Statistical tests showed that slow cooling decreased the SBS value (p<0.01) and showed more cohesive and combined fracture modes while the other cooling methods showed more adhesive failures. These studies indicated that the properties of porcelain to zirconia frameworks may differ from those indicated for metal-ceramic and that the cooling method of the porcelain may interfere with some properties of mono or bilayer structures

Rahabilitación oral sobre implantes instalados por medio de la técnica sin colgajo (flapless) y carga inmediata / Oral rehabilitation with flapless surgical technique and immediate implant loading

La rehabilitación oral con implantes osteointegrados es un tratamiento que está bien documentado y con un alto porcentaje de éxito. Sin embargo, exigencias relacionadas al tiempo de tratamiento y a la técnica quirúrgica fueron surgiendo. En ese contexto, el procedimiento de carga inmediata, en el cual la prótesis dental es instalada inmediatamente después del procedimiento quirúrgico se tornó una práctica constante. A pesar de que la carga inmediata ha sido un importante avance, procedimientos mínimamente invasivos, como la instalación de implantes con la técnica directa, sin desplazamiento del colgajo mucoperiostio (flapless) vienen siendo cada vez más realizados. La asociación de la carga inmediata con la técnica directa o de flapless mejora la aceptación de los pacientes y profesionales, pues no hay necesidad de sutura, además de reducir el edema, la hemorragia durante y después de la cirugía, el dolor post-operatorio, el tiempo quirúrgico, la incomodidad y hematoma, reduciendo también la necesidad de medicación post-operatoria. Esas características facilitan las etapas de rehabilitación inmediatamente después de la colocación de los implantes, colaborando con el trabajo del técnico protésico. De esa forma, la propuesta de este trabajo es presentar un caso clínico de rehabilitación oral con implantes osteointegrados y prótesis fijas en ambas arcadas, donde se realizó la técnica directa seguida por carga inmediata, relatando el diagnóstico, planificación, procedimientos quirúrgico/protésicos y seguimiento de 20 meses

The oral rehabilitation with osseointegrated implants is a well-documented treatment with high rate of success. Nevertheless, demands related to treatment time and surgical technique began to appear. In this context, the procedure of immediate loading in which the dental prosthesis is placed right after implant surgery has become a constant practice. Although immediate loading has been an important advance, minimally invasive procedures, such as implant placement without raising a mucoperiosteal flap (flapless) are increasingly being performed. Association of immediate loading with the flapless technique improves acceptance by patients and professionals, because no suturing is required. Moreover, it reduces swelling, bleeding during and after surgery, postoperative pain, surgery time, discomfort and hematoma, as well as the need for postoperative medication. These characteristics ease the stages of rehabilitation soon after implant placement, cooperating with prosthodontist's work. Thus, the proposal of this study is to present a clinical case of oral rehabilitation with osseointegrated implants and fixed prosthesis in both arches, in which the flapless technique was applied, followed by immediate loading. It will discuss the diagnosis, prosthetic planning, surgical/prosthodontic procedures and follow-up for 20 months

Efeito das dimensões dos corpos de prova na resistência à flexão de compósitos restauradores / Effect of specimen size on flexural strength of restorative composites

O objetivo deste estudo foi avaliar, em relação à norma ISO, o efeito da redução das dimensões dos corpos de prova na resistência à flexão, em três pontos, dos compósitos restauradores de nanopartículas (Filtek Supreme - 3M ESPE) e micro-híbrido (Filtek Z-250 - 3M ESPE). Foram confeccionados 40 corpos de prova para cada material com asseguintes dimensões de comprimento, largura e espessura (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0,8 × 0,8 mm. Os compósitos foram inseridos em único incremento em matrizes metálicas bipartidas, correspondentes a cada dimensão avaliada, e fotoativados. Os corpos de prova foram armazenados a 37 ± 1 °C, em ambiente seco e protegido de luz, durante 7 dias. Posteriormente, foi realizado o ensaio de resistência à flexão, em três pontos, usando o equipamento MTS 810, com célula de carga de 10 kN e velocidade de 0,5 mm/min. Os resultados mostraram variabilidade significativa para as dimensões avaliadas (p = 0,00), com valores, em relação à norma ISO (116,700 MPa), estatisticamente superiores para os corpos de prova de 10 × 1 × 1 mm (142,530 MPa), semelhantes para os de 10 × 2 × 1 mm (115,815 MPa) e inferiores para os de 8 × 0,8 × 0,8 mm (86,650 MPa).Houve igualdade estatística (p = 0,08) para os compósitos estudados (Filtek Supreme, 125,270 MPa; Filtek Z-250, 108,130 MPa). Corpos de prova de 10 × 2 × 1 mm proporcionaram, com menor consumo de material, energia e tempo, valores de resistência à flexão equivalentes àqueles obtidos nas dimensões preconizadas pela norma ISO 4049.

The aim of this study was to evaluate the influence of specimen size, in comparison with the ISO Standard, on the three point flexural strength of resin composite restorative materials Filtek Supreme and Filtek Z-250. Fortyspecimens were fabricated for each material with the following length, width and thickness measurements (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0.8 × 0.8 mm. The composites were inserted in a single increment into two-piece metal device and light-polymerized. The specimens were dry stored at 37 ± 1 °C and protected from light for 7 days. After this period, flexural strength was measured by three-point flexure test using MTS 810 equipment, with a load cell of 10 kN at a speed of 0.5 mm/min. For the evaluated sizes, the results showed significant variability (p = 0.00) with values when compared with the ISO Standard (116.700 MPa), being statistically higher for the test specimens measuring 10 × 1 × 1 mm (142.530 MPa), similar for those of 10 × 2 × 1 mm (115.815 MPa) and lower for those of 8 × 0.8 × 0.8 mm (86.650 MPa). There was statistical equality (p = 0.08) for the studied composites (Filtek Supreme, 125.270 MPa; Filtek Z-250, 108.130 MPa). Specimens measuring 10 × 2 × 1 mm provided flexural strength values equivalent to those obtained in the sizes recommended by the ISO 4049 standard, with lower consumption of material, energy and time.

Previsibilidade de implantes curtos: revisão de literatura / Predictability of short dental implants: a literature review

Introdução: Nas situações clínicas em que ocorre severa reabsorção óssea após perda de dentes, as opções de tratamento com implantes incluem a necessidade de reconstrução óssea prévia e instalação de implantes convencionais ou apenas de implantes curtos. Objetivo: Revisar não sistematicamente a literatura com o propósito de sintetizar e discutir alguns itens sobre o uso de implantes curtos, tais como aspectos biomecânicos, índices de sucesso, longevidade e planejamento cirúrgico-protético. Revisão de literatura: Buscou-se selecionar referências atuais e de impacto acerca dos implantes curtos, comparando-os aos convencionais. Diversos estudos destacam a maior importância do diâmetro dos implantes. Para a prática clínica os curtos apresentam altas taxas de sucesso e previsibilidade quando determinados aspectos biomecânicos são levados em consideração. Conclusão: A colocação de implantes curtos torna-se um tratamento viável para pacientes com altura óssea reduzida.

Introduction: In clinical situations where severe bone resorption has occurred following tooth loss, implant treatment options may comprise either a previous bone reconstruction or only the use of short implants. Objective: This non-systematic review summarizes and discusses some aspects of the use of short implants, such as: biomechanical aspects, success rate, longevity and surgical-prosthetic planning. Literature review: Current and relevant references were selected in order to compare short dental implants to conventional ones. Several studies have highlighted the great importance of wide-diameter implants. Dental short implants have shown high predictability and success rates when some biomechanical aspects are taken into consideration. Conclusion: Placement of short dental implants is a viable treatment method for patients with decreased bone height.

Effect of surface treatments on the bond strength of a resin cement to commercially pure titanium

Investigation of the effectiveness of surface treatments that promote a strong bond strength of resin cements to metals can contribute significantly to the longevity of metal-ceramic restorations. This study evaluated the effect of surface treatments on the shear bond strength (SBS) of a resin cement to commercially pure titanium (CP Ti). Ninety cast CP Ti discs were divided into 3 groups (n=30), which received one of the following airborne-particle abrasion conditions: (1) 50 ?m Al2O3 particles; (2) 30 ?m silica-modified Al2O3 particles (Cojet Sand); (3) 110 ?m silica-modified Al2O3 particles (Rocatec). For each airborne-particle abrasion condition, the following post-airborne-particle abrasion treatments were used (n=10): (1) none; (2) adhesive Adper Single Bond 2; (3) silane RelyX Ceramic Primer. RelyX ARC resin cement was bonded to CP Ti surfaces. All specimens were thermally cycled before being tested in shear mode. Failure mode was determined. The best association was Rocatec plus silane. All groups showed 100 percent adhesive failure. There were combinations that promote higher SBS than the protocol recommended by the manufacturer of RelyX ARC.

A investigação da eficácia de tratamentos de superfície que promovem uma forte resistência de união de cimentos resinosos aos metais pode contribuir significantemente para a longevidade das restaurações metalocerâmicas. Este estudo avaliou o efeito de tratamentos de superfície na resistência ao cisalhamento da união de um cimento resinoso ao titânio comercialmente puro (Ti cp). Noventa discos foram fundidos em Ti cp e divididos em 3 grupos (n=30), os quais receberam uma das seguintes condições de jateamento: (1) partículas de Al2O3 de 50 ?m; (2) partículas de Al2O3 modificadas por sílica de 30 ?m (Cojet Sand); (3) partículas de Al2O3 modificadas por sílica de 110 ?m (Rocatec). Para cada condição de jateamento, os seguintes tratamentos pós-jateamento foram utilizados (n=10): (1) nenhum; (2) adesivo Adper Single Bond 2; (3) silano RelyX Ceramic Primer. O cimento resinoso RelyX ARC foi aplicado à superfície do Ti cp. Todos os espécimes foram termociclados antes do ensaio de cisalhamento. O modo de fratura também foi determinado. A melhor associação foi o Rocatec mais silano. Todos os grupos apresentaram 100 por cento de falha adesiva. Houve combinações que promoveram maior resistência ao cisalhamento da união que aquela recomendada pelo fabricante do RelyX ARC.

Reparo intraoral de próteses metalo-cerâmicas : um relato de caso clínico / Intraoral repair in metal-ceramic prostheses: a clinical report

Repairing fractured metal-ceramic prosthesis is a treatment alternative that can increase the restoration longevity, preserve dental structure, and/or the integrity of implant components, besides being a simple, low-cost technique. However, clinicians often see restoration repair as a challenge because of the many doubts regarding the procedures required to obtain satisfactory results. Therefore, the motivation to write this article is the need to provide instructions for clinicians dealing with a situation involving fractured porcelain, presenting an intraoral repair technique that can be used in cases of a fractured ceramic veneer of a fixed partial prosthesis. The technique consisted in treating the remaining ceramic surface and applying a microhybrid composite resin following the steps of a protocol that, according to scientific evidence, has promoted high bond strength to porcelain, in addition to being cost effective.

O reparo de próteses metaloceramicas, quando a cerâmica encontra-se fraturada, e um tratamento alternativo que pode aumentar a longevidade dessas restaurações, preservar a estrutura dental ou a integridade de componentes protéticos sobre implantes, alem de ser uma técnica simples e de baixo custo. No entanto, essa técnica, geralmente, e vista como um desafio pelos cirurgiões-dentistas uma vez que não ha um protocolo clinico bem estabelecido para a obtenção de resultados satisfatórios. Assim sendo, o objetivo deste artigo e prover instruções para os clínicos lidarem com situações de fratura da cerâmica por meio da apresentação de um caso clinico, no qual uma técnica de reparo intra-oral indicada para essa situação foi empregada. Essa técnica consiste em tratar a superfície da cerâmica remanescente e aplicar uma resina composta microhibrida, seguindo os passos de um protocolo que, de acordo com evidencias cientificas, tem promovido alta resistência de união, alem de apresentar um baixo custo.

Alternativa de design para próteses do tipo Protocolo: relato de caso / Alternative design to Brånemark Protocol prosthesis: case report

A prótese do tipo Protocolo de Brånemark é uma alternativa bem sucedida para a reabilitação de mandíbulas edêntulas com implantes osseointegrados. Porém, grande parte dos pacientes usuários desse tipo de reabilitação incomoda-se com o acúmulo de alimentos sob a barra metálica e com o prejuízo estético causado pelo espaço vazio existente entre a barra e a mucosa. Tais queixas podem ser facilmente resolvidas com a adequação do desenho da prótese. O presente trabalho propõe novos designs para a prótese do tipo Protocolo, através do preenchimento dos espaços entre os cilindros protéticos com resina acrílica. Essas alternativas promovem maior conforto ao paciente, visto que dificultam o acúmulo de restos alimentares, facilitam a higienização e garantem melhorias estéticas, além de favorecer o controle periódico. Apesar da técnica ser de fácil execução, poucos dentistas e técnicos em prótese dentária fazem uso dessas alternativas para o design do Protocolo, deixando de oferecer um tratamento diferenciado ao paciente. Por esse motivo, esse trabalho expõe um caso clínico onde foi confeccionada uma prótese do tipo Protocolo de Brånemark com seu design modificado.

Brånemark Protocol prosthesis is an adequate alternative to the rehabilitation of edentulous mandibles with osseointegrated implants. However, a great number of users bother with the accumulation of food under the metallic bar and the esthetic prejudice due to the existent gap between the bar and the mucosa. Such complaints can be easily solved with the correct design of the prosthesis. This work suggests new designs to this kind of prosthesis through the fulfilling of the gaps between prosthetic cylinders with acrylic resin. These alternatives promote better comfort to the patient, once they make it difficult to accumulate food, facilitate hygiene, maintenance and guarantee esthetic improvements. Despite being easy to make, few dentists and dental prosthesis technicians use these alternative design of protocols, not offering a differentiated treatment to their patients. This work shows a case report where the use of a modified design of the Brånemark protocol was applied.

Carga imediata com utilização de barra de titânio soldada a laser: relato de caso / Immediate Loading with Titanium Bar Submitted to Welded Laser: a Case Report

Um pré-requisito fundamental para as próteses fixas implantossuportadas é a distribuição uniforme de forças ao osso adjacente aos implantes, e isto só é possível quando a adaptação da prótese aos componentes protéticos se dá de uma forma passiva. A ausência desta adaptação é capaz de gerar forças no nível da interface osso-implante, podendo levar a uma remodelação óssea que resulta no deslocamento do implante. Toda esta problemática é ainda mais grave, quando se trata de carga imediata, que é uma técnica caracterizada pela aplicação de cargas aos implantes em até 48 horas após a instalação dos implantes. O presente trabalho tem como objetivo realizar o relato de um caso clínico em que foi realizada a carga imediata sobre uma prótese tipo protocolo com infra-estrutura confeccionada em titânio, sendo esta infra-estrutura soldada com a técnica da solda a laser, possibilitando assim uma melhor adaptação desta prótese e conseqüentemente uma menor transmissão de esforços ao osso adjacente aos implante.

A fundamental prerequisite for implant-supported prosthetics is a uniform distribution of forces on bone adjacent to the implants, and this is only possible when the adaptation of the prosthesis to the prosthetic components occurs in a passive fashion. The absence of this adaptation may generate forces at the level of the bone-implant interface and may lead to a remodeling of bone resulting form the dislocation of the implant. The whole problem is even more serious when an immediate charge is required, which is a technique characterized by the application of forces to the implants in up to 48 hours following the placement of the implants. The purpose of the present paper is to report a clinical case of an immediate charge over a protocol prosthesis with a titanium infrastructure soldered by laser, thereby providing a better adaptation of the prosthesis and consequently a lesser transmission of stress onto the bone adjacent to the implant.

Tubo-Parafuso: uma alternativa viável para próteses fixas implanto-suportadas / The tube-screw technique: an alternative way for implant-supported, fixed prostheses - case report

O protocolo de colocação de implantes osseointegrados propostos por Brånemark no início dos anos de 1980 promoveu um grande impulso da Implantodontia na área odontológica. Porém, com a crescente utilização destes implantes começaram a surgir problemas relacionados à estética e à mecânica dos componentes protéticos, principalmente quando se trata de reabilitações extensas em que a posição dos implantes não permite a realização de próteses parafusadas. A partir daí começou a se buscar uma maneira de corrigir o posicionamento destes implantes sem que a possibilidade de reversibilidade do tratamento fosse perdida, visto que este fator continua sendo determinante para a preferência do sistema de retenção parafusado. Sendo assim, o presente trabalho, através de um caso clínico, tem por objetivo mostrar o sistema tubo-parafuso que, ao mesmo tempo em que permite a correção da inclinação vestibular dos implantes, mantém a reversibilidade do trabalho protético.

Solda a laser em barras de TI na busca da passividade em carga imediata: relato de caso / Laser weld in Ti bars to passivity excellence on immediate loading: case report

A restauração imediata após a colocação do implante dental é uma excelente opção de tratamento que o cirurgião-dentista pode oferecer a seus pacientes. Este procedimento provê uma restauração estável e estética. Durante a sessão de carga imediata, a agilidade dos procedimentos cirúrgicos e protéticos garante um conforto maior ao paciente e à equipe de trabalho. Para isso faz-se interessante usufruir da versatilidade da soldagem a laser dos componentes de uma prótese fixa sobre implante. Durante a soldagem a laser não há contato direto com a área da solda, é um método rápido e promove soldagens precisas e bem definidas, pois a região afetada pelo calor é pequena e o campo magnético não causa efeito sobre o feixe laser. Outro procedimento que vem crescendo nos últimos anos é o uso do titânio na área odontológica. Isto se deve à sua biocompatibilidade, resistência à corrosão, e propriedades físicas e mecânicas melhores em relação às ligas de Co-Cr e Ni-Cr. No entanto, a utilização do titânio em infra-estruturas protéticas tem sido um processo lento. Apesar de suas ótimas características, principalmente quando unidas às vantagens da solda a laser, muitos dentistas e laboratórios não conhecem o material e poucos trabalhos mostram acompanhamento clínico. Neste ínterim, este trabalho expõe um caso clínico de reabilitação oral com prótese sobre implante metaloplástica com infra-estrutura confeccionada em titânio e soldada pela técnica da solda a laser.

The immediate restoration after placing the dental implant is an excellent option for treatment that the dentist can offer your patients. This procedure provides a stable and aesthetic restoration. During the session of immediate load, the agility of surgical and prosthetics procedures guarantees a greater comfort to the patient and team work. Therefore, it is interesting to enjoy the versatility of the laser-welded technique of the components of a prosthesis implant-supported. During the laser welding there is no direct contact with the solder area, is a rapid method and promotes precise and well defined welding, because the region affected by the heat is small and the magnetic field causes no effect on the laser beam. Another procedure that has been growing in recent years is the use of titanium in dentistry. This is due to its biocompatibility, resistance to corrosion, and physical properties better than Co-Cr-Ni-Cr alloy. However, the use of titanium in infrastructure prosthetic has been a slow process. Despite its great features, especially when attached to the benefits of laser welding, many dentists and laboratories do not know the material and there are few longitudinal studies. In the meantime, this work presents a case of oral rehabilitation with prosthetic implant on metaloplastic with titanium framework and the use of laser-welded technique.

Parafusar ou cimentar: qual a melhor opção para as próteses implanto-suportadas? / Cement and screw-retained: which the best option for implant-supported protheses?

O presente trabalho discute as vantagens e desvantagens de se utilizar próteses implanto-suportadas parafusadas ou cimentas analisando os seguintes aspectos: adaptação marginal, retenção, oclusão, estética, instalação, reavaliação e reversibilidade do caso e longevidade

União de dente a implante com conexões rígidas tipo tubo-parafuso: relato de caso clínico / Combination of tooth and implant using tube screw rigid connection: a case report

A literatura mostra que as conexões rígidas apresentam maiores sucessos na união entre dentes e implantes, mas com a desvantagem da perda da reversibilidade. A conexão tubo-parafuso trata-se de uma conexão rígida com reversibilidade.